Flat textile strip forming one layer of a flexible duct that is used for hydrocarbon transport and the duct thus formed

ABSTRACT

The invention relates to a flat textile strip which is made from, for example, a reinforced thermoplastic material. The inventive strip is wound around a tube in order to form one layer of a duct through which a pressurized fluid flows. The invention is characterized in that said strip ( 10 ) comprises a central piece ( 11 ) having a more or less rectangular section and two longitudinal edges ( 12 ) which are thinner than the central piece.

[0001] The present invention relates to a flat tape intended for the manufacture of one layer of a flexible pipe for subsea transport of hydrocarbons and gases, especially an unbonded flexible pipe of the offshore type as defined in the API 17B and 17J recommendations of the American Petroleum Institute.

[0002] Such pipes are formed from layers—partly metallic and partly polymeric—that are not bonded together. These pipes have at least one polymeric pressure sheath surrounded by a pressure vault, at least partly produced by the helical winding of elongate metal elements leaving a slight clearance between their turns called the “inter-turn gap” or “gap” (generally at least one layer of elongate metal elements, especially profiled wires, wound with a short pitch) and one or more plies of reinforcing elements wound with a long pitch.

[0003] One of the problems encountered in practice is creep of the pressure sheath into the gaps existing between the turns of the pressure vault. This creep takes place owing to the combined effect of the internal pressure and of the temperature of the fluid transported in the pipe. Depending on the effluent and its temperature, the plastic sheaths used may, for example, be produced from materials of the polyvinylidene fluoride PVDF type (for example the coatings known under the brand names Coflon® and Gammaflex®, for applications at relatively high temperatures, typically above 80° C.). These materials have a tendency to undergo relatively substantial creep into the inter-turn gaps of the vault. This creep leads to the formation of creep pips in the gaps.

[0004] In dynamic applications, such as in risers, these pips are a source of fracture initiation because of the movements of the vault turns which tend to shear these pips.

[0005] One solution commonly used for trying to solve the creep problems is the production of anticreep layers as described in document FR 2 743 614, which covers the specific end-fitting of such pipes. These layers are expensive in terms of raw materials, but also in terms of production costs.

[0006] Another solution envisioned for solving this problem could consist in using a conventional tape wound with a short pitch around the pressure sheath, the tape being intended to prevent said sheath from creeping. However, this solution is excessively difficult to implement for the following reasons.

[0007] The overlapping of a tape with a unidirectional fiber during short-pitch taping would induce an overstress in the fibers at the overlapping part, resulting in substantial deterioration in the fibers, extending as far as the fracture at the edge of the tape. Such a fracture would then cause the tape to be destroyed, which would no longer fulfil its anticreep function. To avoid these overlaps, it would be necessary to lay the unidirectional tape edge to edge, that is to say without a clearance. However, to wind a tape without a clearance is virtually impossible because of the following reasons: the precision of existing tape winders (pitch control, tension variation in the tape laid, resulting in a variation in tape width), the geometry of the pipe (tolerance on the diameter) and the sag of the pipe (slightly domed shape of the pipe under its own weight during the taping operations in the tape winder), etc.

[0008] The object of the invention is to propose a tape which makes it possible to solve the abovementioned problems, to satisfactorily manage the winding clearances and to achieve satisfactory taping in order to obtain a layer intended to prevent the sheath that covers it from creeping, or, more generally, to produce other windings constituting one layer of a pipe.

[0009] The object of the invention is achieved by means of a flat textile tape, intended to produce, by helical winding, one layer of a flexible pipe for transporting hydrocarbons, serving to convey, especially under water, a pressurized fluid, the pipe consisting of unbonded layers, these being partly metallic and/or made of composites and partly polymeric, characterized in that the textile tape used to produce these windings is a tape having edges that are thinned over a certain width so as to allow an overlap of the thinned edges that does not result in an appreciable overthickness. In other words, the tape is formed from a central section with an approximately rectangular cross section and from two longitudinal edges that are thinner than the central section. Advantageously, the thickness of the edges is uniform and approximately equal to one half of the thickness of the central section; their width is advantageously between 5% and 15%, preferably in the region of 10%, of the width of the central section.

[0010] The thinning of the overlapping edges is known per se, in fields very remote from the invention, for example in assemblies of clinkered boards or from document JP 59035924 which discloses a multilayer resin tape for forming a transparent tube that will then be sectioned to form containers. The tape is produced with thinning of the lateral edges and it is wound without any clearance on itself with welding of the edges. This is the constituent tape of the tube itself, but in no way a tape constituting a single layer of a flexible pipe for hydrocarbons, comprising metal layers and polymeric layers. In addition, the tape is made of a uniform resin and is not a textile tape, the method of manufacture of which is completely different.

[0011] Advantageously, the tape is formed by a single thickness of filament roving having different dimensions in the central part and in the edges.

[0012] Advantageously, the tape is provided with a tracer in the region of the boundary between the central part and the edges so as to be able to visually control the quality of the winding and of the overlap of the edges.

[0013] The invention also relates to the flexible pipe for hydrocarbons, at least one layer of which is obtained by the winding of flat textile tapes according to the invention.

[0014] This relates in particular to a flexible pipe for hydrocarbons, of the unbonded offshore type, and the tape may be used as suggested above for producing an anticreep band between the pressure sheath and the pressure vault, in particular for dynamic-type applications (for risers) and essentially for production pipes (through which a hot fluid flows) which lead to the use of sheaths made of semicrystalline polymer, with creep and fracture problems that this entails and which have already been mentioned. The invention applies most particularly to what are called rough-bore pipes, which are mainly used in production, but also to what are called smooth-bore pipes (the internal carcass being coated with an inner sheath), especially in what are called “kill and choke line” pipes which are small-diameter flexible couplers called “jumpers” located at platforms.

[0015] In the application as an anticreep layer, several layers of tape are generally laid in order to obtain the quantity of fiber necessary for the pressure of creep of the sheath (the plies being offset). The helical winding is preferably carried out with a short pitch. The tape may have any width, but it is preferable to use wide tapes for obvious coverage and manufacturing reasons.

[0016] The textile tape according to the invention may receive other applications and constitute, for example, one or more reinforcing layers wound with a short pitch around tension armor plies of the pipe in order to prevent them from swelling due to the inverse end effect (shortening of the pipe due to the external hydrostatic pressure, causing compression in the armor wires).

[0017] Other features and advantages of the invention will become apparent on reading the following description of several illustrative examples, with reference to the appended drawings in which:

[0018]FIG. 1 is a perspective view of a pipe that includes anticreep layers produced by winding a tape according to the invention;

[0019]FIG. 2 is a perspective view of a first embodiment of a flat tape according to the invention;

[0020]FIGS. 3 and 4 are sectional views of a second and third embodiment of a flat tape according to the invention;

[0021]FIG. 5 is a sectional view of a winding of the tape of the second embodiment, showing the overlap of the edges;

[0022]FIG. 6 is a sectional view of a fourth embodiment of the invention; and

[0023]FIG. 7 is a perspective view of a conventional pipe for transporting hydrocarbons, to which the invention applies.

[0024] The conventional construction of an unbonded flexible pipe for hydrocarbon transport will be briefly recalled with reference to the appended FIG. 7, which shows a pipe of the rough-bore type comprising, from the inside outward: a metal carcass 101, generally produced by an interlocked metal strip wound helically around the axis AA of the pipe and intended to provide crush resistance under external pressure; a polymeric inner sealing sheath 102, called the pressure sheath; a metal pressure vault 111, consisting here conventionally of the helical winding with a short pitch (winding angle generally close to 90° relative to the axis of the pipe) of an interlocked profiled metal wire 103 covered, if necessary, by the short-pitch helical winding of a hoop reinforcement wire 104; armor 105 resistant to axial tension in the longitudinal direction of the pipe and conventionally consisting of one or more pairs of crossed plies 109, 110 in a long-pitch winding (typically less than 60° with respect to the axis of the pipe); and a polymeric outer sealing sheath 108. Other intermediate layers, such as the layers 106, 107, may be provided depending on the type and application of the pipe. Likewise, certain layers may be absent depending on the application for which the pipe is intended. In the case of a smooth-bore pipe, the sealing sheath or pressure sheath constitutes the innermost element of the pipe. The winding of the profiled wire 103, forming the vault located above the pressure sheath, whatever its shape, leaves a certain inter-turn gap allowing the pipe to bend.

[0025]FIG. 1 shows an example of how the invention is applied to the production of an anticreep layer. This shows, highly symbolically, a pipe 1 for transporting pressurized fluids, consisting of the pressure sheath 2 (similar to the layer 102) and a pressure vault 5, (similar to the layer 103), the other layers of the pipe (carcass, armor plies, outer sheath) having been omitted for the sake of clarity of the drawing. Between the pressure sheath 2 and the pressure vault 5 there is a first ply 3 and a second ply 4 of textile tape according to the invention, these being intended to prevent the layer 2 from creeping into the inter-turn gaps of the vault 4. The anticreep plies 3 and 4 are produced by winding a flat tape 10 according to the invention with a short pitch, the lay angle being typically greater than 70°, or even 80°, with respect to the longitudinal axis of the pipe. As may be seen in FIG. 5, the overlap of the edges of the adjacent turns of the tape 10 prevent the formation of through-gaps in the layer obtained.

[0026] FIGS. 2 to 4 show three tape embodiments that differ by the arrangement of the thin edges. For the sake of clarity of the drawings, the width of the edges relative to that of the central section of the tape has been exaggerated in the drawings.

[0027] The tape 10 of the invention, having a mean width L+l, consists of a central section 11 with a rectangular cross section, of width L and thickness E, flanked laterally by two longitudinal edges or flanges 12, with a width l and thickness e. It is preferable that: e=E/2 and L/20<l<3L/20.

[0028] The flanges 12 may be placed at mid-height of the edges of the central section 11 (FIG. 2), either so as to alternate at the top and bottom of the two edges of the central section 11 (FIGS. 3 and 5) or exclusively at the bottom (or at the top) of the two edges of the central section 11, or in any other arrangement. Although the arrangement shown in FIGS. 3 and 5 is that which lends itself most naturally to the overlapping of the edges 12, the other arrangements are suitable in practice, owing to the flexibility of the tape and to its deformation during winding.

[0029] As shown in FIG. 2, and, more schematically, in FIGS. 3 to 5, the tape of the invention is a textile tape formed from layers of filament rovings 14 held in place by binding means 15. It is formed, for example, in accordance with the teaching of document EP 0 853 547, from layers of filament rovings 14 joined together and held in place by binding means 15 and a bonding material so as to maintain a high overall density, for example at least 39%. The bonding material, for example a thermoplastic, coating the filament rovings has not been shown. However, the tape may also be formed only by the weaving of filament rovings with a weft yarn, but with no bonding material. In the case of a woven tape with no bonding material, the density is advantageously kept high, for example at least 39%. The filament rovings 14 used as warp yarn may be of any type, such as those made of aramid (Kevlar®, Twaron® or Technora®) or made of carbon, for example. The edges 12 are made of the same material as the central section, simply with a smaller thickness, and therefore for example with a fewer number of layers of filament rovings. According to the invention, it is advantageous for the binding means (weft yarns) to be spaced out so as, when the pipe bends, to allow the wound tapes to untwist and their longitudinal fibers to be reorganized. Alternatively, the edges may be produced from fibers having physical or chemical characteristics different from those of the central part. In particular, it will be possible to use fibers whose elongation at break is greater than that of the fibers used in the central part. It will also be possible to use fibers that differ in the nature or the degree of twisting of the filament rovings used, or a different density.

[0030] As illustrated in FIG. 5, the tape 10 of the invention makes it possible to accommodate the overall clearance during taping, by at least partially overlapping the edges 12 of the adjacent tapes. This at least partial overlapping of the edges 12 prevents the formation of through-gaps (over the entire thickness of the reinforcing layer) between two tapes. At the very most, a gap 13 smaller than the width l of the edge is formed, which gap is not a through-gap. In FIG. 1, this gap 13 has been shown only for the first turn.

[0031] The embodiment of the tape 10 of FIG. 6 differs from that of FIG. 2 in that, instead of being produced by several thicknesses of filament rovings, it is produced only by weaving in two dimensions (warp yarns and weft yarns), with a single thickness of filament rovings 14, 14′. The rovings 14 of the central part 11 are of larger size than the rovings 14′ of the thin edge parts 12.

[0032] It is also advantageous to provide a tracer on the tape 10, for example a colored yarn 16, which allows the position of the tape during winding to be displayed. This yarn 16 is advantageously placed between the edge 12 and the central part 11 of the tape 10 (this yarn has been illustrated only in FIG. 6, but it may apply to all the embodiments) in order to define the interface. Thus, it is possible to visually check that no tape edge 12 overlaps a central tape part 11 (there must always be two tracers 16 side by side; no tracer 16 must be covered if the winding has been carried out correctly).

[0033] Only the application to the production of an anticreep layer between pressure sheath and pressure vault of the pipe has been shown in detail, but the tape according to the invention may be used for other layers of a pipe, especially a reinforcing layer wound around armor plies 109, 110 of the pipe shown in FIG. 7, or between these plies 109, 110. 

1. A flat textile tape, intended to produce, by helical winding, one layer of a flexible pipe for transporting hydrocarbons, serving to convey, especially under water, a pressurized fluid, the pipe consisting of unbonded layers, these being partly metallic and/or made of composite material and partly polymeric, characterized in that the tape (10) is formed from a central section (11) of approximately rectangular cross section and from two longitudinal edges (12) that are thinner than the central section.
 2. The tape as claimed in claim 1, characterized in that the thickness of the longitudinal edges (12) is approximately equal to one half of the thickness of the central section (11).
 3. The tape as claimed in either of the preceding claims, characterized in that the width of the edges (12) is between 5% and 15% of the width of the central section (11).
 4. The tape as claimed in any one of the preceding claims, characterized in that the density of the tape is equal to or greater than 39%.
 5. The tape as claimed in any one of the preceding claims, characterized in that it is formed from filament rovings held together by binding means and a thermoplastic bonding material.
 6. The tape as claimed in any one of claims 1 to 5, characterized in that it is formed by a single thickness of filament rovings (14, 14′) having different dimensions in the central part (11) and in the edges (12).
 7. The tape as claimed in any one of claims 1 to 6, characterized in that the tape (10) is provided with a tracer (16) in the region of the boundary between the central part (11) and the edges (12).
 8. A pipe for transporting hydrocarbons, used for conveying, especially under water, a pressurized fluid, the pipe consisting of unbonded layers, these being partly metallic and/or made of composites and partly polymeric, the pipe comprising at least one layer formed by a helical winding of a flat textile tape (10), characterized in that the tape (10) is formed from a central section (11) having an approximately rectangular cross section and from two longitudinal edges (12) that are thinner than the central section, the tape (10) being wound with at least partial overlapping of the lateral edges (12).
 9. The pipe as claimed in claim 8, characterized in that the lay angle of the tapes (1) is typically greater than 70°, or even 80°.
 10. The pipe as claimed in either of claims 8 and 9, characterized in that the edges (12) of the tape (10) are produced from fibers having physical or chemical characteristics different from those of the central part (11).
 11. The pipe as claimed in any one of claims 8 to 10, which includes a pressure sheath (2) and a pressure vault (5), characterized in that the layer made from tape (10) is an anticreep layer wound between the pressure sheath (2) and the pressure vault (5) of the pipe (1).
 12. The pipe as claimed in any one of claims 8 to 10, characterized in that the layer made from tape (10) is a reinforcing layer wound around an armor ply (109, 110) of the pipe or between the armor plies (109, 110). 